"Room-temperature stress-strain curves are presented for compression, tension, and shear loadings on four compositions of tungsten carbide with cobalt binder. Values of modulus of elasticity, modulus of rigidity, Poisson's ratio in the elastic region, ultimate strength, density, and hardness for the four materials are tabulated" (p. 1).
Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.
"Room-temperature stress-strain curves are presented for compression, tension, and shear loadings on four compositions of tungsten carbide with cobalt binder. Values of modulus of elasticity, modulus of rigidity, Poisson's ratio in the elastic region, ultimate strength, density, and hardness for the four materials are tabulated" (p. 1).
This report is part of the following collections of related materials.
National Advisory Committee for Aeronautics Collection
The National Advisory Committee for Aeronautics (NACA) was a U.S. federal agency founded on March 3, 1915 to undertake, promote, and institutionalize aeronautical research. On October 1, 1958 the agency was dissolved, and its assets and personnel transferred to the newly created National Aeronautics and Space Administration (NASA).
The Technical Report Archive & Image Library (TRAIL) identifies, acquires, catalogs, digitizes and provides unrestricted access to U.S. government agency technical reports. The mission of TRAIL is to ensure preservation, discoverability, and persistent open access to government technical publications regardless of form or format.
Johnson, Aldie E., Jr.Mechanical Properties at Room Temperature of Four Cermets of Tungsten Carbide with Cobalt Binder,
report,
December 1954;
(https://digital.library.unt.edu/ark:/67531/metadc57319/:
accessed June 11, 2024),
University of North Texas Libraries, UNT Digital Library, https://digital.library.unt.edu;
crediting UNT Libraries Government Documents Department.