"A series of glass compositions containing uranium oxide was investigated to determine fiberizability and physical properties of resultant fibers. The basic properties to be determined were the maximum U/sub 3/O/sub 8/ content in a fiberizable glass and the maximum service temperature of the fibers. Glasses containing 60 wt% U/sub 3/O/sib 8/ were fiberizable; the fibers had strengths of 100,000 psi at 1600 deg F. Fiber-forming equipment was installed at Moun Laboratory to produce glass fibers containing PuO/sub 2/. Fibers were successfully formed in the first trials. For additional work a series of base glasses were provided affording a wider range …
continued below
We've identified this
report
as a primary source within our collections. Researchers, educators, and students may find this report useful in their work.
Provided By
UNT Libraries Government Documents Department
Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.
Added Title:
Atomic Energy Commission Report NYO-9735
Description
"A series of glass compositions containing uranium oxide was investigated to determine fiberizability and physical properties of resultant fibers. The basic properties to be determined were the maximum U/sub 3/O/sub 8/ content in a fiberizable glass and the maximum service temperature of the fibers. Glasses containing 60 wt% U/sub 3/O/sib 8/ were fiberizable; the fibers had strengths of 100,000 psi at 1600 deg F. Fiber-forming equipment was installed at Moun Laboratory to produce glass fibers containing PuO/sub 2/. Fibers were successfully formed in the first trials. For additional work a series of base glasses were provided affording a wider range of both PuO/sub 2/ solubility and physical properties."
This report is part of the following collections of related materials.
TRAIL Microcard Collection
Imaged from microcard, these technical reports describe research performed for U.S. government agencies from the 1930s to the 1960s. The reports were provided by the Technical Report Archive and Image Library (TRAIL).
The Technical Report Archive & Image Library (TRAIL) identifies, acquires, catalogs, digitizes and provides unrestricted access to U.S. government agency technical reports. The mission of TRAIL is to ensure preservation, discoverability, and persistent open access to government technical publications regardless of form or format.