The relation of structure to lack of superconductivity in Pr-Ba-Cu-O was systematically investigated. First, the phase equilibria of this system was studied to find the processing parameters which maximize the cation-site ordering between Pr and Ba ions. Second, a comparative study between superconducting Nd-Ba-Cu-0 and non- superconducting Pr-Ba-Cu-0 was performed by forming solid-solution Nd- Pr-Ba-Cu-0. The relation between structure and superconductivity in Nd{sub 1{minus}x}Pr{sub x}Ba{sub 2}Cu{sub 3}O{sub 7{minus}{delta}} is investigated. {Tc} decreases monotonically with increasing {times} and superconductivity disappears at around x=0.3-0.4. {Tc} is enhanced by 10K when the sample is processed at an oxygen partial pressure (PO{sub 2}) of …
continued below
Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.
Descriptive information to help identify this thesis or dissertation.
Follow the links below to find similar items on the Digital Library.
Description
The relation of structure to lack of superconductivity in Pr-Ba-Cu-O was systematically investigated. First, the phase equilibria of this system was studied to find the processing parameters which maximize the cation-site ordering between Pr and Ba ions. Second, a comparative study between superconducting Nd-Ba-Cu-0 and non- superconducting Pr-Ba-Cu-0 was performed by forming solid-solution Nd- Pr-Ba-Cu-0. The relation between structure and superconductivity in Nd{sub 1{minus}x}Pr{sub x}Ba{sub 2}Cu{sub 3}O{sub 7{minus}{delta}} is investigated. {Tc} decreases monotonically with increasing {times} and superconductivity disappears at around x=0.3-0.4. {Tc} is enhanced by 10K when the sample is processed at an oxygen partial pressure (PO{sub 2}) of 0.01 atm, followed by oxygenation at 450C. Depression of {Tc} as a function of {times} and PO {sub 2} is explained in terms of a charge-transfer model. It is suggested that destruction of superconductivity in the RE{sub 1{minus}x}Pr{sub x}Ba{sub 2}CU{sub 3}O{sub 7{minus}{delta}} (RE=rare-earth) system can be viewed as disruption of four-fold planar coordinated Cu ions in the chain-site due to permanent occupation of extra Pr ions on Ba sites.
Physical Description
75 p.
Notes
OSTI as DE94014231; Paper copy available at OSTI: phone, 865-576-8401, or email, reports@adonis.osti.gov
This document is part of the following collection of related materials.
Office of Scientific & Technical Information Technical Reports
Reports, articles and other documents harvested from the Office of Scientific and Technical Information.
Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.
Minseo, P.The relationship of structure to superconductivity in the Pr-Ba-Cu-O system,
thesis or dissertation,
May 10, 1994;
Iowa.
(https://digital.library.unt.edu/ark:/67531/metadc1390127/:
accessed May 27, 2024),
University of North Texas Libraries, UNT Digital Library, https://digital.library.unt.edu;
crediting UNT Libraries Government Documents Department.