This technical report presents measurements of the thermal expansion of five titanium carbide type cermets from 68 to 1800F. These cermets are designated by Kennametal, Inc., as K 138A, K 150A, K 152B and K 162B. They contain from 64 to 80 weight percent titanium carbide, 10 to 30 weight percent metal binder and 6 to 10 weight percent other carbides. The metal binders are cobalt, nickel, and nickel and molybdenum. An attempt was made to calculate the thermal expansion of each type cermet from thermal expansions of the constituents. The expansion of the mixture was computed by weighting and …
continued below
We've identified this
report
as a primary source within our collections. Researchers, educators, and students may find this report useful in their work.
Provided By
UNT Libraries Government Documents Department
Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.
Added Title:
Pratt & Whitney Aircraft Company Report CNLM-4234
Description
This technical report presents measurements of the thermal expansion of five titanium carbide type cermets from 68 to 1800F. These cermets are designated by Kennametal, Inc., as K 138A, K 150A, K 152B and K 162B. They contain from 64 to 80 weight percent titanium carbide, 10 to 30 weight percent metal binder and 6 to 10 weight percent other carbides. The metal binders are cobalt, nickel, and nickel and molybdenum. An attempt was made to calculate the thermal expansion of each type cermet from thermal expansions of the constituents. The expansion of the mixture was computed by weighting and expansions of the constituents according to (1) weight percent of the constituents, (2) volume percent of the constituents and (3) according to a value developed for mixtures by P. S. Turner. It was found that expansions computed according to volume percent and by Turner's method agreed with measured values with +- 5 percent. The values calculated by weight percent were from 5 to 11 percent higher than the observed values. The thermal expansions of these cermets are compared with the expansions of a group of metals and alloys.
This report is part of the following collections of related materials.
TRAIL Microcard Collection
Imaged from microcard, these technical reports describe research performed for U.S. government agencies from the 1930s to the 1960s. The reports were provided by the Technical Report Archive and Image Library (TRAIL).
The Technical Report Archive & Image Library (TRAIL) identifies, acquires, catalogs, digitizes and provides unrestricted access to U.S. government agency technical reports. The mission of TRAIL is to ensure preservation, discoverability, and persistent open access to government technical publications regardless of form or format.
Harrington, L. C. & Rowe, G. H.The Thermal Expansion of Five Titanium Carbide Cermets from 68 to 1800F,
report,
August 17, 1962;
Washington D.C..
(https://digital.library.unt.edu/ark:/67531/metadc1256438/:
accessed May 27, 2024),
University of North Texas Libraries, UNT Digital Library, https://digital.library.unt.edu;
crediting UNT Libraries Government Documents Department.