Stress-Corrosion Cracking Problems in the Homogeneous Reactor Test

Description: Chloride-induced stress-corrosion cracking has been encountered in the Homogeneous Reactor Test during the preliminary testing. The rector is constructed of austenitic stainless steels. It is unique in that it will operate at 250 to 300 C with an aqueous uranyl sulfate solution fuel containing 200 to 500 ppm of dissolved oxygen. The cracking has occurred in a secondary system used for detecting leaks in the flanged joints of the primary systems and in the grooves of flanges in the primary syste… more
Date: January 31, 1957
Creator: Bohlmann, E. G. & Adamson, G. M.
Partner: UNT Libraries Government Documents Department
open access

Quarterly Report of the Solution Corrosion Group for the Period Ending January 31, 1957

Description: A second test of the mockup of the Zircaloy - stainless steel transition joint as used in the HRT reactor vessel has been completed. The joint and bellows have now received 104 thermal cycles and 148 mechanical deflections. The joint and bellows have functioned properly; corrosion damage has been negligible, except for a small area on the bellows which has undergone pitting attack. Long-term runs with uranyl sulfate solutions of the concentration proposed or use in the HRT have shown the soluti… more
Date: January 31, 1957
Creator: Griess, J. C. F.; Savage, H. C.; English, J. L.; Greeley, R. S.; Buxton, S. R.; Hess, D. N. et al.
Partner: UNT Libraries Government Documents Department
open access

Carbon Steel in High Temperature Water

Description: Resistance of carbon steel to corrosion in oxygenated high-temperature (250C) water was unexpectedly good at high oxygen concentration. Pertinent literature, critically examined, and toroid experiments indicted that at low oxygen concentration attack did increase with concentration, but as oxygen concentration was sufficiently increased, more protective films were formed on the metal. Some corrosion factors in the application of carbon steel to nuclear reactors systems are discussed.
Date: January 31, 1957
Creator: Moore, G. E.
Partner: UNT Libraries Government Documents Department
open access

Metallurgical Examination of HRT Leak Detector Tubing and Flanges

Description: After several failures had occurred in the HRT leak detector system, several lengths of this tubing were removed for metallurgical examination. The tubing was of type 304 stainless steel and was 1/4" in diameter with a 0.065 wall. The tubing had been purchased as three different lots, the first in 45 ft. lengths and the other two as standards lengths. Tubing from the first lot was used primarily for the shield penetration and, therefore, sections of it are present in all lines of the system. It… more
Date: January 31, 1957
Creator: Adamson, G. M; Hammond, T. M.; Kegley, T. M. & White, J. K.
Partner: UNT Libraries Government Documents Department
open access

Comments on the Determination of the Particle Size Distribution of Thorium Oxide

Description: Factors affecting the results of thoria particle size distribution measurements by sedimentation procedures currently and recently employed are considered. The effects of thoria concentration, solvent, dispersant, thoria properties, and other factors are discussed.
Date: March 31, 1957
Creator: Moore, G. E.
Partner: UNT Libraries Government Documents Department
open access

Effects of Letdown Rates and Oxygen Injection Rates on Xenon Poison Level and Excess Oxygen Concentration in the HRT

Description: Calculations indicate that it is impossible, even at high oxygen injection rates, to insure an excess of oxygen in the HRT fuel solution if the bubble letdown rate is more than 1 or 2 liters per minute. If, on the other hand, no bubbles are allowed to form, a reasonable excess oxygen concentration can be maintained with an oxygen injection rate which would not tax the capacity of the off-gas system. The xenon poison will be reduced to less than 2% by liquid letdown alone, and if an iodine absor… more
Date: May 31, 1957
Creator: Haubenreich, P. N.
Partner: UNT Libraries Government Documents Department