In-reactor corrosion of X-8001 and 1245 aluminum: Analysis of data from PT IP-42A
Description:
Failures of standard fuel element jackets (1245 aluminum alloy) after relatively short Hanford reactor exposures are occurring at high reactor power levels. Metallographic examination of fuel element jackets from short exposure ruptures shows the cause of failure to be rapid intergranular corrosion. This type of attack has been reproduced in laboratory tests by exposure to water at temperatures above 200 C, or to steam at temperatures higher than 300 C. Flow disruptions due to misalignment of t…
more
Date:
June 25, 1958
Creator:
Dillon, R. L. & Richman, R. B.